Polyethylene

Polyethylene

0200 (LDPE)

0200 (LDPE)

LF0200 is a high molecular weight low density polyethylene film grade combining good flexible extrusion behavior and superior mechanical properties. Film made from LF0200 exhibits high dart impact combined with excellent yield and tensile strength and high stiffness. 

Its toughness bears even in cold temperatures. The film can be sealed on all types of machines.The film possesses good dimensional stability and is resistant to tearing and breaking. LF0200 contains antioxidant. 

Application:

  • Greenhouse Film
  • Industrial Shrink Film
  • 25kg Industrial Bags for re-packing powdered foods and grains such as rice, pulses, salt, sugar, flour and cereals
  • Bags for packing powdered substances for domestic or industrial use such as detergents, sand and grave

s l1600

 

#Property UnitTypical ValueTest Method
1 MFI (190℃/2. 16 kg)​ gr/10 min 2 ASTM D 1238
2 Density  gr/ml 0.920 * TSTM 209 B
3 Softening Point  94  ASTM D 1525
4 Haze  % 15 max  ASTM D 1003
5 Gloss @ 60 Gu 60 min ASTM D 523
6 Elongation @ break (MD) % 330 min  ASTM D 882
7 Elongation @ break (TD) % 600 min  ASTM D 882 
8 Tensile @ break (MD) Kg/cm2 160 min  ASTM D 882
9 Dart impact Gr 100 min  ASTM D 1709

Processing Conditions:

LF0200 can be easily processed in all types of extruders. The temperature of the polymer at the die output should be in the range of 160-180 o C. Minimum blow up ratio should be about 2 in order to keep a good balance of mechanical properties. To avoid blocking and shrinkage in the reel, the film temperature at the nip rollers and haul off should be kept as close as possible to the ambient temperature.

Storage: The product should be stored in dry conditions at temperature below 60 o C and protected from UV light.Improper storage can initiate degradation with resulting odour generation and colour changes.

Health & Environment:

LF0200 is not classified as a dangerous product.Dust and fines from the product may give a risk for dust explosion. All equipment should be properly grounded. Inhalation of dust may irritate the respiratory system and should be avoided. During processing of the product small amounts of fumes are generated, which require proper ventilation.

Recycling:

The product is suitable for recycling using modern methods of shredding and cleaning for other applications only if approved in the relevant standard or specification. In-house production waste should be kept clean to facilitate direct recycling. Dumping and land filling is also possible in agreement with the competent authorities.

Food Contact: The composition of products complies with the EC Directive 90.128.EEC for use in food contact applications.

Packaging:

This product is packed in 25 Kg PE bags.

 


For technical assistance or further information on this product contact our technical team

2420H (LDPE)

2420H (LDPE)

2420 H is a non -additivated,low density Polyethylene.It is delivered in pellet form.

Application:

  • Bags & pouches
  • Film
  • Shrink Film
  • Blown Film
  • Cast Film


Shrink film

Processing Method:

  • Cast Film
  • Blown Film

 

Features:

  • Good Heat Sea
  • Optical
  • Good Processability
  • Food grade

 

#Property Value Unit Test Method
1 Melt Flow rate (MFR)(190°C/2.16Kg) 1.9 g/10 min ISO 1133
2 Density 0.924 g/cm3 ISO 1183
3 Tensile Modulus 260 MPa ISO 527-1, -2
4 Tensile Stress at Yield 11 MPa ISO 527-1, -2
5 Tensile Strength at Break MD/TD 26/8 MPa ISO 527-1, -3
6 Tensile Strain at Break MD/TD 260/600 % ISO 527-1, -3
 7 Dart Drop Impact (50 blown Film) 110 ASTM D 1709
 8 Vicat softening temp (A50 (50 °C/h 10N))​ 94  ℃  ISO 306
9 Haze (50) ≤8.0 % ASTM D 1003
10 Gloss (60 ͦ,50) ≥100   ASTM D 2457

 

Packaging:

Supplied in pellet form and packaged in 25 Kg bags.

Storage:

Polyethylene products (in pelletized or powder form) should not be stored in direct sunshine and/or heat radiation. Ultraviolet causes a change in the materials properties. The Storage area should be dry and preferably not exceed 50 °C. Under cool, dry, dark conditions polyolefin resins are expected to maintain the original properties for at least 18 month. FM Plastics cannot be held responsible for diminishing qualities due to poor storage conditions, such as; color change, foul smell etc. Generally, it is considered best to process PE resin within 6 months after delivery.

Handling:

Ensure proper ventilation of the work environment to minimize health and safety hazards from fine particles. Ensure machinery and equipment is properly grounded to prevent sparks that can ignite dust. Molten polymers will cause thermal injuries to organic matter please ensure safety glasses and appropriate safety apparel is worn.


For technical assistance or further information on this product contact our technical team.

CRP 100 (HDPE)

CRP 100 (HDPE)

HM‐CRP100 (Natural and Black) is a high density polyethylene with 1‐Butene as co monomer. It is natural, outstanding ESCR, high impact strength, outstanding hydrostatic strength for PE 100 class.

Application:

  • Pipes
  • Water Pipes
  • Gas Pipes
  • Pressure Pipes

HDPE Pipe

#Test/CompositionValue UnitMethod
1 MFI @190°C, 5.0Kg 0.22 gr/10 min ASTM 1238
2 MFI @ 190°C, 21.6Kg 6.2 gr/10 min ASTM 1238
3 FRR (21.6/5.0) 28 ----- ----
4 Mass Density((23°C) 0.957 gr/cm3 ISO 1183-1
5 Bulk Density 0.605 gr/cm3 ASTM D 1829
6 Carbo Black Content  2.3 % ASTM D 4218
7 Carbon Black Dispersion  Max 3 Rating  BS-2782
8 Impact Strength (Charpy Index @ 23°C) >20 MJ/mm2 ISO 179/1eA
9 Hydrostatic Strength (80°C /5.5 MPa) >165 HR ISO 11677
10 Volatiles  349 ppm Basel Method 
11 Contamination  2 Rating  Hoechst Method
12 Vicat Softening Temperature ,(B50) 75 °C ASTM D D1525
13 Oxidation Induction Time ,(210 °C) >25 min  ASTM D 3895
14 DSC Melting Point  130 °C ---------
15 Shore Hardness ,(Shore D,3 Sec) 63 --------- ASTM D 2240

 Storage and Handling

The material is packed in 25 kg bags or in bulk containers protecting it from contamination. Storage times of natural materials longer than 6 months may have a negative influence on the quality of the final product (for example the brightness). It is generally recommended to convert all materials latest within 6 months from the date of delivery. The material is subjected to degradation by ultra‐violet radiation or by high storage temperatures. Therefore the material must be protected from direct sunlight, temperatures above 40°C and high atmospheric humidity during storage. Further unfavourable storage conditions are large fluctuations in ambient temperature and high atmospheric humidity. These conditions may lead to moisture condensing inside the packaging. Under these circumstances, it is recommended to dry the material before use. Unfavourable storage conditions may also intensify the material´s slight characteristic odour.


For technical assistance or further information on this product contact our technical team.

0209AA  (LLDPE)

0209AA (LLDPE)

“LL0209AA” is a LLDPE copolymer with butene as comonomer which contains anti- oxidant. It is recommended for general purpose applications. It is suitable for blending with conventional LDPE.

Film made from pure LL 02090 AA has the following advantages over conventional LDPE:

  • Better sealing, higher puncture resistance
  • Greater drawdown capability
  • Higher tensile strength

Neutralizer: Calcium Stearate

Antioxidant: Irganox1010, Irganox168

Application:

  • Heavy duty sacks
  • Agricultural films
  • Liners 
  • Stretch film

LLDPE 209A

Features:

  • Good Tensile Strength
  • Good Drawdown Ability
  • Good Puncture Resistance
  • Good Seal Properties
  • Food Grade
#Property Value Unit Test Method
1 MFR (190 ℃ /2 16 kg) 0.9 g/10 min  ISO 1133
2 Density  920 Kg/m3 ISO 1183
3 Tensile Strength at Yield MD/TD 10/11 MPa  ISO 527
4 Tensile Strength at Break MD/TD  41/32 MPa ISO 527
5 Elongation at Break MD/TD  620/840 % ISO 527
6 Tear Strength MD/TD  145/370  g/25µ ASTM D1922
7 Dart Drop Impact  150  g ASTM D 1709

 

Processing Condition:

Recommended melt temperature: 180-225 °C

Film Blowing Machine: Dr.Collin 30M (Extruder) +180/400(Unit)

Zone Temperature: 200 °C

Hopper Temperature: 180 °C

Screw speed is set to 50 rpm The feeder of the extruder is cooled by cooling water CWS/CWR (35-45 °C)

Blow up ratio: 2 Die

Diameter: 75 mm Die Gap: 1.2 mm


For technical assistance or further information on this product contact our technical team.

52505 (HDPE)

52505 (HDPE)

52505 is a HDPE copolymer which is manufactured in gas phase process. This grade is an injection molding grade for applications requiring a good physical property even at low temperatures, like pails, containers and technical moldings.

Application:

  • Containers

HDPE 52505

Features and Addetives:

  • Good physical property even at low temperatures
  • HD-52505:Thermal Antioxidant
  • HD-52505UV:Thermal Antioxidant UV Stabilizer

 

#Resin PropertiesVALUEUNIT Method
1 Melt Index(21.6) 5 g/10 min D1238
2 Density 0.952 g/cm³ D1505
3 Thermal Properties​ Value  UNIT  METHOD
4 Vicat Softening Point​ 124 D1525
5 Molded Properties Unit  Typical Value Test Method 
6 Flexural Modulus MPa  1200 D790
7 Tensile Strength at Yield MPa 27 D638
8 Tensile Strength at Break MPa 13 D638
9 H.D. T 67 D1922
10 Notched Izod Impact @ 23 °C J/m 29 D256/A

Additive: HD-52505: Thermal Antioxidant
HD-52505UV: Thermal Antioxidant UV Stabilizer


 

Handellling and Health Safety

Molten polymers could be injured skin or eye so safety glasses and appropriate gloves are suggested to prevent possible thermal injuries. Also appropriate ventilation is suggested in working by melt polymer. Accumulation of fines or dust particles that are in this grade is not suitable because of explosion hazard probability. So adequated filters and grounding exists at all time are recommended.

Storage

Polyethylene products (in pelletised or powder form) should not be stored in direct sunshine and/or heat radiation. Ultraviolet cause a change in the material properties.The Storage area should be dry and preferably don't exceed 50 °C. Under cool, dry, dark conditions Polymers polyolefin resins are expected to maintain the original material and processing properties for at least 18 month. Manufacturer would not ressponsible about quality diminishing such as color change, bad smell or ets which caused by bad storage conditions. It is better to process PE resin within 6 months after delivery

packaging:

Polyolefin resins are supplied in pllet form packed in 25kg bags. Alternative packaging modes are avalable for selected grades.

 

For technical assistance or further information on this product contact our technical team.

 
EX3 (HDPE)

EX3 (HDPE)

EX3 (HM 5010 T2N) is a natural colored high density polyethylene with Butene-1 as comonomer. The product is classified as PE 80 and good stress crack resistance properties (ESCR) combined with good impact strength. Stabilization: Ca-Stearate, Zn-Stearate, Irganox1010, Irgafos168.

EX3  is suitable for extrusion into a full range of pipe and fittings sizes, where high density resins are required.
EX3  is suitable for use in transport of a wide range of fluids for industrial, rural and mining applications.
Suitability for use in any application should be determined by appropriate performance testing.

Application:

  • Pipe Extrusion PE80 Class
  • Pressure pipe
  • Drinking water and gas pipes
  • Sewer pipes and their fittings
  • Discharge pipes For injection moulded and other fittings
  • Sheets

EX3

 

Features:

  • Good Environmental Stress Crack Resistance (ESCR)
  • Food Contact
  • Good Chemical Resistance
  • High Molecular Weight
#PropertyValue Unit Method
1 MFR (190℃/5 kg) 0.45±0.05 g/10 min ISO 1133
2 MFR (190℃/21.6 kg) 12.0±3.0 g/10 min ISO 1133
3 FRR (21.6/5) 28±4 --------  -------
4 Density 0.945±0.002 g/cm3 ISO 1183
5 Notched Impact Strength  >12 MJ/mm2 ISO 179/1eA
6 Pipe Evaluation Hydrostatic Strength (80℃ 4N/mm2) 1000min  Hours (DIN 8074 & Din 8075 & ISO 1167)

 


For technical assistance or further information on this product contact our technical team.

0209KJ (LLDPE)

0209KJ (LLDPE)

“LL0209KJ” is a LLDPE copolymer with butene as comonomer which contains anti- oxidant. It is recommended for general purpose applications. It is suitable for blending with conventional LDPE.

Film made from pure LL 02090 KJ has the following advantages over conventional LDPE:

  • Better sealing, higher puncture resistance
  • Greater drawdown capability
  • Higher tensile strength

LL0209KJ offers high slip film with easy opening properties when used pure in thickness range 35-100 microns. Addition of other polymers, master batches and pigments or use of other thickness may alter film slip and anti-block performance.

 

Application:

  • Heavy duty sacks
  • Agricultural films
  • Liners 
  • Stretch film

LLDPE 209KJ

Features:

  • Good Tensile Strength
  • Good Drawdown Ability
  • Good Puncture Resistance
  • Good Seal Properties
  • Food Grade

 

 

#Property Value Unit Test Method
1 Melt Flow Index (200℃ -5KG) 0.9 g/10 min  ASTM D-1238​
2 Density  0.921 gr/cm3 ASTM D-1505
3 Vicat Softening Point 105 ASTM D-1525
4 FILM**      
5 Dart Drop Impact          Method 140 GR ASTM D-1709
6 Tensile Stress at Yield    MD/TD 10/11 MPa ASTM D-882
7 Tensile Stress at Break    MD/TD 41/32 MPa  ASTM D-882
8 Elongation at Break        MD/TD  620/840 % ASTM D-882`
9 Haze                                    - % 12 ASTM D-1003
10 Gloss (45℃)​                         -  %  56  ASTM D-2457

 

Processing Condition:

Recommended melt temperature: 180-225 °C

Film Blowing Machine: Dr.Collin 30M (Extruder) +180/400(Unit)

Zone Temperature: 200 °C

Hopper Temperature: 180 °C

Screw speed is set to 50 rpm The feeder of the extruder is cooled by cooling water CWS/CWR (35-45 °C)

Blow up ratio: 2 Die

Diameter: 75 mm Die Gap: 1.2 mm


For technical assistance or further information on this product contact our technical team.

7000F (HDPE)

7000F (HDPE)

7000F is a high molecular weight, high density polyethylene copolymer which has a broad molecular weight distribution. The design of the product, molecular architecture and density, gives it a unique combination of easy extrusion and high melt strength with strong physical properties which makes it suitable for producing thin films with excellent strength and rigidity. 

Application:

  • Films
  • Film with Public Use
  • Shopping bags
  • Heavy duty bags
  • Food packaging bag
  • Industrial bags
 

blog details1 medium

 

Properties: 

  • Recommend film thickness at 10-25 micron
  • High tensile strength with good dart impact strength
  • Low gel content
  • Good moisture barrier
  • Enhanced ultra-thin film
  • Food contact applicable
  • High stiffness
  • Wide service Temperature range, UV resistance
  • Good impact resistance and processability
#PHYSICALVALUEUNITMETHOD
  Resin Properties   
1 Melt Flow Rate 0.04 g/10 min ASTM D 1238
2 Density 0.952 g/cm3 ASTM D 1183
  Film Properties   
1 ESCR 600 h ASTM D1693
2 Izod Impact Strength, Notched 294 J / m ASTM D256
3 Tensile Elongation at Break 500 % ASTM D638
4 Tensile Strength at Break 38.24 MPa ASTM D638
5 Tensile Strength at Yield 24.51 MPa ASTM D638
  THERMAL   
1 Melting Point 131 C ° ASTM D2117

Process conditions:

Typical processing conditions for 7000F are:

Melt Temperature: 200 - 215°C Frost line Height: 6-8 times die Ø

Packing:

25 Kg plastic bags 

Big bag with specified weight 

 

Storage and Handling:

Pellets are packed in 25 kg PE-LD bags and transported on stretch or shrink-wrapped pallets at eligible load of polymer 1375 kg. Heat treated pallets are available as well. We use adhesive between the bags in order to avoid their slipping. Pay attention to this fact during the removing of the bags from the pallets. The prefered method is to lift the bag at first without rotation. Transportation in a road silo or rail silo is also available. Since polyethylene is a combustible substance, the fire safety rules applicable for combustible materials in warehouses and store rooms should be observed. If polymer is stored in conditions of high humidity and fluctuating temperatures, then atmospheric moisture can condense inside the packing. If it happened, it is recommended the pellets to be dried before use. During the storage polyethylene should not be exposed to UV radiation and temperatures above 40°C. Producer does not take responsibility for any damages caused by adverse storage.

Reach Statement:

Polymers are exempt of REACH registration. However, their raw materials which mean monomers and relevant additives have been registered. We are committed to fully respect legislation and will only use REACH compliant raw materials. At this point in time TIPELIN does not contain any substances specifically identified as SVHC at levels greater than 0.1%.

 

For technical assistance or further information on this product contact our technical team.


 

EX5 (HDPE)

EX5 (HDPE)

     The monkey-rope is found in all whalers; but it was only in the Pequod that the monkey and his holder were ever tied together. This improvement upon the original usage was introduced by no less a man than Stubb, in order to afford the imperilled harpooneer the strongest possible guarantee for the faithfulness and vigilance of his monkey-rope holder.In the tumultuous business.
So strongly and metaphysically did I conceive of my situation then, that while earnestly watching his motions, I seemed distinctly to perceive that my own individuality was now merged in a joint stock company of two; that my free will had received a mortal wound; and that another's mistake or misfortune might plunge innocent me into unmerited.
SEE ALSO: 5 Joomla templates get new goodies and a performance boost
Being the savage's bowsman, that is, the person who pulled the bow-oar in his boat (the second one from forward), it was my cheerful duty to attend upon him while taking that hard-scrabble scramble upon the dead whale's back. You have seen Italian organ-boys holding a dancing-ape by a long cord.
The Idea
In the tumultuous business of cutting-in and attending to a whale, there is much running backwards and forwards among the crew. Now hands are wanted here, and then again hands are wanted there. There is no staying in any one place; for at one and the same time everything has to be done everywhere..

“In the tumultuous business of cutting-in and attending to a whale, there is much running backwards and forwards among the crew. Now hands are wanted here, and then again hands are wanted there. There is no staying in any one place; for at one and the same”


I have hinted that I would often jerk poor Queequeg from between the whale and the ship—where he would occasionally fall, from the incessant rolling and swaying of both. But this was not the only jamming jeopardy he was exposed to. Unappalled by the massacre made upon them during the night, the sharks now freshly and more keenly allured by the before pent blood which began to flow from the carcass—the rabid creatures swarmed round it like bees in a beehive.Being the savage's bowsman.blog details1 medium
Taking email back
Being the savage's bowsman, that is, the person who pulled the bow-oar in his boat (the second one from forward), it was my cheerful duty to attend upon him while taking that hard-scrabble scramble upon the dead whale's back. You have seen Italian organ-boys holding a dancing-ape by a long cord. Just so, from the.

  • The monkey-rope is found in all whalers; but it was only in the Pequod that the monkey and hi.
  • The monkey-rope is found in all whalers; but it was only in the Pequod that the monkey and hi.
  • The monkey-rope is found in all whalers; but it was only in the Pequod that the monkey and hi.

The monkey-rope is found in all whalers; but it was only in the Pequod that the monkey and his holder were ever tied together. This improvement upon the original usage was

It was a humorously perilous business for both of us. For, before we proceed further, it must be said that the monkey-rope was fast at both ends; fast to Queequeg's broad canvas belt, and fast to my narrow leather one. So that for better or for worse, we two, for the time, were wedded; and should poor Queequeg sin.

#PropertyVALUEUNITMethod
1 MFR (190℃ /5 kg) 0.28±0.07 g/10 min ISO 1133
2 MFR(190℃ /21.6 kg) 8.0±2.0 g/10 min ISO 1133
3 FRR (21.6/5) ------- ----  
4 Density 0.949±0.002 g/cm3 ISO 1183

 


he bow-oar in his boat (the second one from forward), it was my cheerful duty to attend upon him while taking that hard-scrabble scramble upon the dead whale's back. You have seen Italian organ-boys holding a dancing-ape by a long cord. Just so, from the ship's steep side, did I hold Queequeg down there in the sea, by what is technically called in the fishery a monkey.

1922T (LDPE)

1922T (LDPE)

LDPE 1922T is Low Density Polyethylene for Injection Moulding. 

The grade especially developed for applications requiring a good balance between flow properties and mechanical properties.1922T is a special grade produced by the tubular process.

Application:

  • Toys
  • Houseware
  • Snap-on lids

LDPE 1922T

 

Features:

  • Good Drawdown Ability
  • Good Mechanical Properties
  • Food Contact
  • Good Flowability

 

#Physical ValueUnitTest Condition
1 Density 0.919 g/cm3 -
2 High Load Melt Flow Index (190℃/ 2.16 kg) 22 g/10min At 2.16Kg Load, 190. C
3 MFI 75 g/10min  At 5Kg Load, 190. C
4 MVR 29 g/10min At 2.16Kg Load, 190. C
5 MVR 98 g/10min At 5Kg Load, 190. C
6 MECHANICAL      
7 ESCR 3 h  -
8 Hardness Ball Indentation 16 MPa  Applied load 49 N
9 Hardness Shore D 45 -  -
10 Izod Impact, Notched 42 kJ / m²  at + 23. C
11 Izod Impact, Notched 5 kJ / m²  at -30. C
12 Tensile Creep Modulus 80 MPa  after 1 hour
13 Tensile Creep Modulus 4  MPa  after 1000 hours
14 Tensile Elongation at Break 400  %  
15 Tensile Modulus 175  MPa  
16 Tensile notched impact strength 86  kJ / m² at 8.4% elevation at break & 16Ma maximum voltage
17 Tensile Strength at Break 7  MPa  
18 Tensile Strength at Yield 8  MPa  
19 Thermal      
20 Enthalpy change 104  J/g  
21 Heat Deflection Temperature 39  °C  At 0.46MPa
22 Melting Temperature 105  °C  
23 Vicat Softening Point 82  J/g  10N, VST / A

 

Certificates:

  • Food Grade Certificate
  • European Pharmacopeia Statement
  • Toys Requirements; European Standard 71-3
  • RoHS & Brominated Flame Retardant; 2011/65/EU & 2002/96/EC
  • Heavy Metal; EC Directive 94/62/EC on Packaging and Packing Waste
  • Halogens; IEC 61249-2-21
  • Phthalates; Directive 2005/84/EC

For technical assistance or further information on this product contact our technical team.

BL3 (HDPE)

BL3 (HDPE)

HF-4760(BL3) is a blow molding grade resin with high density polyethylenee with 1-Butene as co monomer which is manufactured by the suspension polymerization of ethylene monomer. Stiffness, good ESCR are it's spetial properties. High rigidity and good flowablity which made it proper for usage in bottles and small blow molding goods.

Application:

  • Small blow moulding bottles
  • Containers (up to 5 lit )
  • Packing of pharmaceuticals & surfactants
  • Sheets for thermoforming

BL3

Features:

  • High density and stiffness
  • Good flowabilitty and impact strength
  • Good stress cracking resistance
  • High rigidity
  • Good flow ability

 

 

# PropertiesTypical ValueUnitTest Method
1 MFI @ 190°C, 5 kg 1 gr/10min 53735
2 Density 0.954 gr/ml 53479
3 Notched Impact Strength ≥6.5 MJ/mm2​  53453
4 ESCR, Plax (70°C, 0.5bar) ≥2 HR Hoechst HDPE 19
5 Standard Yellow Index ≤4​ - 6167

 

Handellling and Health Safety

Molten polymers could be injured skin or eye so safety glasses and appropriate gloves are suggested to prevent possible thermal injuries. Also appropriate ventilation is suggested in working by melt polymer. Accumulation of fines or dust particles that are in this grade is not suitable because of explosion hazard probability. So adequated filters and grounding exists at all time are recommended.

Storage

Polyethylene products (in pelletised or powder form) should not be stored in direct sunshine and/or heat radiation. Ultraviolet cause a change in the material properties.The Storage area should be dry and preferably don't exceed 50 °C. Under cool, dry, dark conditions polymers polyolefin resins are expected to maintain the original material and processing properties for at least 18 month. . We would not ressponsible about quality diminishing such as color change, bad smell or ets which caused by bad storage conditions. It is better to process PE resin within 6 months after delivery.

packaging

Polymers Polyolefin resins are supplied in pllet form packed in 25kg bags. Alternative packaging modes are avalable for selected grades.

HB0035 (HDPE)

HB0035 (HDPE)

HB0035 is a high molecular weight high density polyethylene blow moulding grade combining blow moulding extrusion behavior and superior mechanical properties. Blow moulded items made from HB0035 exhibit high impact strength and good stress cracking resistance and high stiffness.

HB0035 contains antioxidant to protect the polymer from degradation during processing. HB0035 is a highly crystalline, non-polar thermoplastic and has excellent chemical resistance and superb impact resistance at ambient conditions and even at cold temperatures. 

Application:

  • Small blow moulding bottles 
  • Containers (up to 5 lit )

0035

 

Features: 

  • High Impact Strength
  • Good Environmental Stress Crack Resistance (ESCR)
  • Good Stiffness
  • Good Chemical Resistance
  • High Molecular Weight
#PropertyUnitTypical ValueTest Method
1 MFI (190 ℃/2. 16 kg) gr/10min  0.35  ASTM D 1238
2 Density   gr/cm3  0.959  ASTM D  1505
3 Izod impact strength  Kg.cm/cm  25 min  ASTM D 256
4 Yellow index  -- -5 max   ASTM D 1925
5 Ash content WT.% 0.06 max   ASTM D 1063
6 Volatile matter WT.% 0.05 max  ASTM D 1960
7 Tensile strength @ break gr/cm2 290 min  ASTM D 638
8 Elongation @ break % 900 min  ASTM D 638
9 Melting point 130 ASTM D 2117
10 Vicat softening point 126 ASTM D 1525
11 ESCR HR 15 ASTM D 1693

Process conditions:

HB0035 can be processed in most types of blow moulding equipment including HDPE or LDPE extruders . It is suitable for producing hollow article in extrusion blow moulding process . A single screw extruder with a barrel of 25D to 30D long , smooth walled grooved feed section and/ or with decompression , mixing and shearing sections with 20D to 25Dscrew length are typical extruders for blow moulding of containers . This arrangement minimizes thermal degradation of melt and provides a high plasticizing capacity coupled with good extrudate quality.


For technical assistance or further information on this product contact our technical team.

Address

Ercument Batanay Sk. Dumankaya Ikon Sit.
A2 Bl. N. 14 B/287 Atasehir – Istanbul, Turkey

Support

Need Any Help
Contact Us

© 2018 Tayebi Worldwide Trading. All Rights Reserved.

Design & Developed by Tayebi IT Team

Hi! Click one of our representatives below to chat on WhatsApp or send us email to support@jahantt.com.tr

  Chat with us on WhatsApp  
Close and go back to page