“LL0209KJ” is a LLDPE copolymer with butene as comonomer which contains anti- oxidant. It is recommended for general purpose applications. It is suitable for blending with conventional LDPE.
Film made from pure LL 02090 KJ has the following advantages over conventional LDPE:
- Better sealing, higher puncture resistance
- Greater drawdown capability
- Higher tensile strength
LL0209KJ offers high slip film with easy opening properties when used pure in thickness range 35-100 microns. Addition of other polymers, master batches and pigments or use of other thickness may alter film slip and anti-block performance.
Application:
- Heavy duty sacks
- Agricultural films
- Liners
- Stretch film
Features:
- Good Tensile Strength
- Good Drawdown Ability
- Good Puncture Resistance
- Good Seal Properties
- Food Grade
| # | Property | Value | Unit | Test Method |
|---|---|---|---|---|
| 1 | Melt Flow Index (200℃ -5KG) | 0.9 | g/10 min | ASTM D-1238 |
| 2 | Density | 0.921 | gr/cm3 | ASTM D-1505 |
| 3 | Vicat Softening Point | 105 | ℃ | ASTM D-1525 |
| 4 | FILM** | |||
| 5 | Dart Drop Impact Method | 140 | GR | ASTM D-1709 |
| 6 | Tensile Stress at Yield MD/TD | 10/11 | MPa | ASTM D-882 |
| 7 | Tensile Stress at Break MD/TD | 41/32 | MPa | ASTM D-882 |
| 8 | Elongation at Break MD/TD | 620/840 | % | ASTM D-882` |
| 9 | Haze - | % | 12 | ASTM D-1003 |
| 10 | Gloss (45℃) - | % | 56 | ASTM D-2457 |
Processing Condition:
Recommended melt temperature: 180-225 °C
Film Blowing Machine: Dr.Collin 30M (Extruder) +180/400(Unit)
Zone Temperature: 200 °C
Hopper Temperature: 180 °C
Screw speed is set to 50 rpm The feeder of the extruder is cooled by cooling water CWS/CWR (35-45 °C)
Blow up ratio: 2 Die
Diameter: 75 mm Die Gap: 1.2 mm
For technical assistance or further information on this product contact our technical team.