“LL0209AA” is a LLDPE copolymer with butene as comonomer which contains anti- oxidant. It is recommended for general purpose applications. It is suitable for blending with conventional LDPE.
Film made from pure LL 02090 AA has the following advantages over conventional LDPE:
- Better sealing, higher puncture resistance
- Greater drawdown capability
- Higher tensile strength
Neutralizer: Calcium Stearate
Antioxidant: Irganox1010, Irganox168
Application:
- Heavy duty sacks
- Agricultural films
- Liners
- Stretch film
Features:
- Good Tensile Strength
- Good Drawdown Ability
- Good Puncture Resistance
- Good Seal Properties
- Food Grade
| # | Property | Value | Unit | Test Method |
|---|---|---|---|---|
| 1 | MFR (190 ℃ /2 16 kg) | 0.9 | g/10 min | ISO 1133 |
| 2 | Density | 920 | Kg/m3 | ISO 1183 |
| 3 | Tensile Strength at Yield MD/TD | 10/11 | MPa | ISO 527 |
| 4 | Tensile Strength at Break MD/TD | 41/32 | MPa | ISO 527 |
| 5 | Elongation at Break MD/TD | 620/840 | % | ISO 527 |
| 6 | Tear Strength MD/TD | 145/370 | g/25µ | ASTM D1922 |
| 7 | Dart Drop Impact | 150 | g | ASTM D 1709 |
Processing Condition:
Recommended melt temperature: 180-225 °C
Film Blowing Machine: Dr.Collin 30M (Extruder) +180/400(Unit)
Zone Temperature: 200 °C
Hopper Temperature: 180 °C
Screw speed is set to 50 rpm The feeder of the extruder is cooled by cooling water CWS/CWR (35-45 °C)
Blow up ratio: 2 Die
Diameter: 75 mm Die Gap: 1.2 mm
For technical assistance or further information on this product contact our technical team.