LDPE 1922T is Low Density Polyethylene for Injection Moulding.
The grade especially developed for applications requiring a good balance between flow properties and mechanical properties.1922T is a special grade produced by the tubular process.
Application:
- Toys
- Houseware
- Snap-on lids
Features:
- Good Drawdown Ability
- Good Mechanical Properties
- Food Contact
- Good Flowability
| # | Physical | Value | Unit | Test Condition |
|---|---|---|---|---|
| 1 | Density | 0.919 | g/cm3 | - |
| 2 | High Load Melt Flow Index (190℃/ 2.16 kg) | 22 | g/10min | At 2.16Kg Load, 190. C |
| 3 | MFI | 75 | g/10min | At 5Kg Load, 190. C |
| 4 | MVR | 29 | g/10min | At 2.16Kg Load, 190. C |
| 5 | MVR | 98 | g/10min | At 5Kg Load, 190. C |
| 6 | MECHANICAL | |||
| 7 | ESCR | 3 | h | - |
| 8 | Hardness Ball Indentation | 16 | MPa | Applied load 49 N |
| 9 | Hardness Shore D | 45 | - | - |
| 10 | Izod Impact, Notched | 42 | kJ / m² | at + 23. C |
| 11 | Izod Impact, Notched | 5 | kJ / m² | at -30. C |
| 12 | Tensile Creep Modulus | 80 | MPa | after 1 hour |
| 13 | Tensile Creep Modulus | 4 | MPa | after 1000 hours |
| 14 | Tensile Elongation at Break | 400 | % | |
| 15 | Tensile Modulus | 175 | MPa | |
| 16 | Tensile notched impact strength | 86 | kJ / m² | at 8.4% elevation at break & 16Ma maximum voltage |
| 17 | Tensile Strength at Break | 7 | MPa | |
| 18 | Tensile Strength at Yield | 8 | MPa | |
| 19 | Thermal | |||
| 20 | Enthalpy change | 104 | J/g | |
| 21 | Heat Deflection Temperature | 39 | °C | At 0.46MPa |
| 22 | Melting Temperature | 105 | °C | |
| 23 | Vicat Softening Point | 82 | J/g | 10N, VST / A |
Certificates:
- Food Grade Certificate
- European Pharmacopeia Statement
- Toys Requirements; European Standard 71-3
- RoHS & Brominated Flame Retardant; 2011/65/EU & 2002/96/EC
- Heavy Metal; EC Directive 94/62/EC on Packaging and Packing Waste
- Halogens; IEC 61249-2-21
- Phthalates; Directive 2005/84/EC
For technical assistance or further information on this product contact our technical team.
Categories (Petrochemical)
Connect
Stay With Us
Subscribe to our news letter to get the lattst
new on Business
new on Business